Mullite(3Al2O3.2SiO2)Castable Refractory
|
|
|
 |
Properties |
 |
|
| Brand Properties |
HR-ASA |
HR-ASB |
| Chemical Composition (%) |
Al2O3 |
¡Ý78 |
¡Ý75 |
| SiO2 |
¡Ü20 |
5-10 |
| SiC |
- |
¡Ý5 |
| Max service temperature (¡ãC) |
1600 |
1500 |
| Bulk density after burnt at 110¡ãC (g/cm3) |
¡Ý2.6 |
¡Ý2.4 |
| Linear changing after burnt at 1500¡ãC¡Á3h (%) |
0.1~ -0.6 |
0.1~ -0.6 |
| Compressive/Bending Strength (MPa) |
110¡ãC¡Á24h |
¡Ý50/¡Ý7 |
¡Ý50/¡Ý7 |
| 1100¡ãC¡Á3h |
¡Ý60/¡Ý8 |
¡Ý60/¡Ý8 |
| 1500¡ãC¡Á3h |
¡Ý90/¡Ý12 |
¡Ý90/¡Ý12 |
| Water content for construction by weight ( % ) |
5-7 |
5-7 |
| Usage |
Hood,Cement kiln |
| Test standard |
YB/T5202-2003 |
| Packing |
25kg plastic bag |
|
|
|
|